| Items |
 /Asset/ULTEMGF.jpg 8430-3751212 ULTEM® 2300 - 30% Glass Filled Polyetherimide Sheet |
/Asset/ULTEMGF.jpg 8430-5001212 ULTEM® 2300 - 30% Glass Filled Polyetherimide Sheet |
/Asset/ULTEMGF.jpg 8430-7501212 ULTEM® 2300 - 30% Glass Filled Polyetherimide Sheet |
/Asset/ULTEMGF.jpg 8430-10001212 ULTEM® 2300 - 30% Glass Filled Polyetherimide Sheet |
/Asset/ULTEMGF.jpg 8430-12501212 ULTEM® 2300 - 30% Glass Filled Polyetherimide Sheet |
|||||
| Sheet Size | 12 x 12 in | |||||||||
| Thickness | 0.375 in | 0.500 in | 0.750 in | 1.000 in | 1.250 in | |||||
| Weight | 2.95 lb/ft² | 3.92 lb/ft² | 5.89 lb/ft² | 7.86 lb/ft² | 9.82 lb/ft² | |||||
| Specific Gravity (ASTM D792) | 1.51 | |||||||||
| Hardness - Rockwell (ASTM D785) | M114 | |||||||||
| Water Absorption - 24 hrs, 73°F (ASTM D570) | 0.16 % | |||||||||
| Water Absorption - Equilibrium, 73°F (ASTM D570) | 0.9 % | |||||||||
| Tensile Strength at Yield - 73°F (ASTM D638) | 24500 psi | |||||||||
| Tensile Strength at Break - 73°F | 23000 psi | |||||||||
| Tensile Modulus - 73°F (ASTM D638) | 1300000 psi | |||||||||
| Elongation at Break, 73°F (ASTM D638) | 3 % | |||||||||
| Flexural Strength - 73°F (ASTM D790) | 33000 psi | |||||||||
| Flexural Modulus (482ºF/250ºC) | 1300000 psi | |||||||||
| Compressive Strength at Yield, 73°F (ASTM D695) | 30700 psi | |||||||||
| Compressive Modulus | 938000 psi | |||||||||
| Shear Strength - Ultimate, 73°F | 14000 psi | |||||||||
| Impact Strength, Notched at 73°F (ASTM D256) | 2 ft·lb/in | |||||||||
| Impact Strength, Un-notched | 8 ft·lb/in | |||||||||
| Coefficient of Linear Thermal Expansion | 1.1 x 10-5 in/in/ºF | |||||||||
| Deflection Temperature at 66 psi, 0.250" (ASTM D648) | 414 ºF | |||||||||
| Deflection Temperature at 264 psi, 0.250" (ASTM D648) | 410 ºF | |||||||||
| Flammability Rating (UL 94) | V0 | |||||||||
| Dielectric Strength - In Air (ASTM D149) | 770 V/m | |||||||||
| Dielectric Strength - In Oil (ASTM D149) | 630 V/m | |||||||||
| Volume Resistivity - 0.062" (ASTM D257) | 3.0 x 1016 ohm·cm | |||||||||
|
|
||||||||||