LDPE is created by free radical polymerization. The high degree of branches with long chains gives molten LDPE unique and desirable flow properties.
Items |
2830-0300 Low Density Polyethylene - (Natural) Rod |
2830-0500 Low Density Polyethylene - (Natural) Rod |
2830-0700 Low Density Polyethylene - (Natural) Rod |
2830-0900 Low Density Polyethylene - (Natural) Rod |
2830-1000 Low Density Polyethylene - (Natural) Rod |
|||||
Weight | N/A 0.020 lb/ft | N/A 0.044 lb/ft | N/A 0.078 lb/ft | N/A 0.119 lb/ft | N/A 0.178 lb/ft | |||||
Density (ASTM D792) | N/A 57.39 lb/ft³ | |||||||||
Hardness - Durometer - Shore D (ASTM D2240) | N/A 55 | |||||||||
Hardness - Rockwell (ASTM D785) | N/A 41 - 50 | |||||||||
Tensile Strength at Break (ASTM D638) | N/A 1943 psi | |||||||||
Tensile Modulus (ASTM D638) | N/A 41615 psi | |||||||||
Tensile Elongation, Break | N/A 515 % | |||||||||
Flexural Modulus | N/A 28565 psi | |||||||||
Izod Impact | N/A No Break | |||||||||
Tensile Impact Strength (DIN 53448) | N/A 401 ft·lb/in² | |||||||||
Heat Deflection Temperature at 66 psi | N/A 100 - 121 ºF | |||||||||
Maximum Operating Temperature | N/A 160 ºF | |||||||||
Volume Resistivity (ASTM D257) | N/A > 1015 ohm·cm | |||||||||
Standard Length | N/A 10 ft4 ft8 ft | |||||||||
|