Polyethylene or polyethylene is a thermoplastic commodity heavily used in consumer products (over 60M tons are produced worldwide every year). Its name originates from the monomer ethane, also known as ethylene, used to create the polymer. Polyethylene stock shapes are classified into three different categories based mostly on its density and branching. The mechanical properties of PE depend significantly on variables such as the extent and type of branching, the crystal structure, and the molecular weight.

LDPE is created by free radical polymerization. The high degree of branches with long chains gives molten LDPE unique and desirable flow properties.

PE2
Unit of Measure
Items PE2
2825-1251212
Low Density Polyethylene - (Natural) Sheet
PE2
2825-1871212
Low Density Polyethylene - (Natural) Sheet
PE2
2825-2501212
Low Density Polyethylene - (Natural) Sheet
PE2
2825-3751212
Low Density Polyethylene - (Natural) Sheet
PE2
2825-5001212
Low Density Polyethylene - (Natural) Sheet
Sheet Size N/A 12 x 12 in
Thickness N/A 0.125 in N/A 0.187 in N/A 0.250 in N/A 0.375 in N/A 0.500 in
Weight N/A 0.63 lb/ft² N/A 0.94 lb/ft² N/A 1.26 lb/ft² N/A 1.89 lb/ft² N/A 2.52 lb/ft²
Density (ASTM D792) N/A 57.39 lb/ft³
Hardness - Durometer - Shore D (ASTM D2240) N/A 55
Hardness - Rockwell (ASTM D785) N/A 41 - 50
Tensile Strength at Break (ASTM D638) N/A 1943 psi
Tensile Modulus (ASTM D638) N/A 41615 psi
Tensile Elongation, Break N/A 515 %
Flexural Modulus N/A 28565 psi
Izod Impact N/A No Break
Tensile Impact Strength (DIN 53448) N/A 401 ft·lb/in²
Heat Deflection Temperature at 66 psi N/A 100 - 121 ºF
Maximum Operating Temperature N/A 160 ºF
Volume Resistivity (ASTM D257) N/A > 1015 ohm·cm